| Property |
Min |
Max |
Unit |
| Price |
4.13 |
4.13 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27500 |
28000 |
MPa |
| Tensile strength |
215 |
440 |
MPa |
| Elongation |
13 |
55 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
|
|
|
| Bending strength |
|
|
|
| Hardness |
55 |
110 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
140 |
290 |
MPa |
| Thermal expansion |
22.9 |
23 |
e-6/K |
| Thermal conductivity |
130 |
150 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
500 |
640 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2770 |
2800 |
kg/m³ |
| Resistivity |
0.018 |
0.021 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
0.2 |
12 |
mm |
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Cu 4.4, Mg 1.5, Mn 0.6 (wt.%)) |
|