| Property |
Min |
Max |
Unit |
| Price |
4.59 |
4.59 |
EURO |
| Young's modulus |
70000 |
72000 |
MPa |
| Shear modulus |
27500 |
28000 |
MPa |
| Tensile strength |
480 |
530 |
MPa |
| Elongation |
2 |
8 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
|
|
|
| Bending strength |
|
|
|
| Hardness |
90 |
140 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
390 |
450 |
MPa |
| Thermal expansion |
23 |
23.4 |
e-6/K |
| Thermal conductivity |
130 |
160 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
480 |
640 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2850 |
2850 |
kg/m³ |
| Resistivity |
0.019 |
0.023 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
6 |
12 |
mm |
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Zn 5.5, Mg 2.5, Cu 1.6, Cr 0.25, Mn 0.15 (wt.%)) |
|