| Property |
Min |
Max |
Unit |
| Price |
1.83 |
2.29 |
EURO |
| Young's modulus |
72000 |
73000 |
MPa |
| Shear modulus |
27000 |
27500 |
MPa |
| Tensile strength |
230 |
250 |
MPa |
| Elongation |
2 |
9 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
60 |
90 |
MPa |
| Bending strength |
|
|
|
| Hardness |
75 |
110 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
190 |
200 |
MPa |
| Thermal expansion |
21 |
22 |
e-6/K |
| Thermal conductivity |
160 |
170 |
W/m.K |
| Specific heat |
970 |
970 |
J/kg.K |
| Melting temperature |
557 |
582 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
-50 |
450 |
°C |
| Density |
2650 |
2650 |
kg/m³ |
| Resistivity |
0.022 |
0.024 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
1 |
20 |
mm |
| Shrinkage |
0.8 |
1 |
% |
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Si 7, Mg 0.3, Fe 0.2, Mn 0.1, Zn 0.1, Cu 0.05 (wt.%)) |
|