| Property |
Min |
Max |
Unit |
| Price |
1.83 |
2.29 |
EURO |
| Young's modulus |
70000 |
75000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
140 |
160 |
MPa |
| Elongation |
0.5 |
1 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
50 |
70 |
MPa |
| Bending strength |
|
|
|
| Hardness |
60 |
80 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
100 |
160 |
MPa |
| Thermal expansion |
21 |
21 |
e-6/K |
| Thermal conductivity |
100 |
130 |
W/m.K |
| Specific heat |
|
|
|
| Melting temperature |
490 |
600 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
15 |
°C |
| Density |
2750 |
2750 |
kg/m³ |
| Resistivity |
0.011 |
0.018 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
2 |
20 |
mm |
| Shrinkage |
0.5 |
1.1 |
% |
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Si 8.0, Cu 3.0, Zn 1.2, Fe 0.8, Mn 0.4, Mg 0.2 (wt.%)) |
|