| Property |
Min |
Max |
Unit |
| Price |
1.83 |
2.29 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
140 |
150 |
MPa |
| Elongation |
2 |
2 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
60 |
70 |
MPa |
| Bending strength |
|
|
|
| Hardness |
50 |
60 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
9 |
100 |
MPa |
| Thermal expansion |
24 |
24 |
e-6/K |
| Thermal conductivity |
110 |
150 |
W/m.K |
| Specific heat |
|
|
|
| Melting temperature |
570 |
630 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
150 |
°C |
| Density |
2600 |
2600 |
kg/m³ |
| Resistivity |
0.016 |
0.022 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
|
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
20 |
mm |
| Shrinkage |
0.8 |
1.5 |
% |
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Mg 3.0, Si 0.5, Fe 0.5, Mn 0.2, Zn 0.1, Cu 0.05 (wt.%)) |
|