| Property |
Min |
Max |
Unit |
| Price |
1.83 |
2.29 |
EURO |
| Young's modulus |
72000 |
75000 |
MPa |
| Shear modulus |
27500 |
28000 |
MPa |
| Tensile strength |
140 |
160 |
MPa |
| Elongation |
1 |
4 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
95 |
95 |
MPa |
| Bending strength |
|
|
|
| Hardness |
50 |
55 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
80 |
90 |
MPa |
| Thermal expansion |
21 |
22 |
e-6/K |
| Thermal conductivity |
120 |
150 |
W/m.K |
| Specific heat |
970 |
970 |
J/kg.K |
| Melting temperature |
533 |
580 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
-50 |
150 |
°C |
| Density |
2650 |
2650 |
kg/m³ |
| Resistivity |
0.015 |
0.022 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
0.8 |
1.1 |
% |
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Si 12, Cu 1.0, Fe 0.8, Mg 0.3, Mn 0.3 (wt.%)) Good corrosion resistance. Typical used for applications in contact with water. |
|