| Property |
Min |
Max |
Unit |
| Price |
1.11 |
1.25 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
70 |
130 |
MPa |
| Elongation |
5 |
33 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
20 |
40 |
MPa |
| Bending strength |
|
|
|
| Hardness |
20 |
35 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
110 |
110 |
MPa |
| Thermal expansion |
24 |
24 |
e-6/K |
| Thermal conductivity |
220 |
220 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
658 |
660 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2710 |
2710 |
kg/m³ |
| Resistivity |
0.028 |
0.028 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al > 99.5 (wt.%)) |
|