| Property |
Min |
Max |
Unit |
| Price |
|
|
|
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
25000 |
25000 |
MPa |
| Tensile strength |
276 |
420 |
MPa |
| Elongation |
4 |
25 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
130 |
138 |
MPa |
| Bending strength |
|
|
|
| Hardness |
50 |
58 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
138 |
393 |
MPa |
| Thermal expansion |
24 |
24 |
e-6/K |
| Thermal conductivity |
120 |
123 |
W/m.K |
| Specific heat |
900 |
904 |
J/kg.K |
| Melting temperature |
577 |
638 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2650 |
2650 |
kg/m³ |
| Resistivity |
0.056 |
0.056 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
|
|
|
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Mg 4.5, Mn 0.4 (wt.%)) |
|