| Property |
Min |
Max |
Unit |
| Price |
|
|
|
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
|
|
|
| Tensile strength |
300 |
340 |
MPa |
| Elongation |
20 |
24 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
120 |
124 |
MPa |
| Bending strength |
|
|
|
| Hardness |
80 |
80 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
175 |
195 |
MPa |
| Thermal expansion |
20 |
22 |
e-6/K |
| Thermal conductivity |
170 |
170 |
W/m.K |
| Specific heat |
880 |
882 |
J/kg.K |
| Melting temperature |
554 |
650 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2750 |
2750 |
kg/m³ |
| Resistivity |
0.04 |
0.04 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
|
|
|
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Cu 2.6, Si 0.5, Mg 0.3 (wt.%)) |
|