| Property |
Min |
Max |
Unit |
| Price |
|
|
|
| Young's modulus |
69000 |
69000 |
MPa |
| Shear modulus |
|
|
|
| Tensile strength |
230 |
340 |
MPa |
| Elongation |
12 |
24 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
115 |
117 |
MPa |
| Bending strength |
|
|
|
| Hardness |
70 |
70 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
228 |
228 |
MPa |
| Thermal expansion |
23 |
23 |
e-6/K |
| Thermal conductivity |
180 |
180 |
W/m.K |
| Specific heat |
897 |
897 |
J/kg.K |
| Melting temperature |
560 |
650 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2710 |
2710 |
kg/m³ |
| Resistivity |
0.035 |
0.035 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
|
|
|
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Si 1.1, Mg 0.6, Mn 0.4 (wt.%)) |
|