| Property |
Min |
Max |
Unit |
| Price |
|
|
|
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27500 |
27500 |
MPa |
| Tensile strength |
240 |
280 |
MPa |
| Elongation |
1 |
3 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
80 |
80 |
MPa |
| Bending strength |
|
|
|
| Hardness |
85 |
90 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
180 |
220 |
MPa |
| Thermal expansion |
23 |
23 |
e-6/K |
| Thermal conductivity |
|
|
|
| Specific heat |
|
|
|
| Melting temperature |
550 |
650 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2750 |
2750 |
kg/m³ |
| Resistivity |
|
|
|
| Breakdown potential |
|
|
|
| Electrochemical potential |
|
|
|
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Cu 4.50, Ti 0.22, Mg 0.20, Si 0.20, Fe 0.20, Zn 0.10, Mn 0.05 (wt.%)) |
|