| Property |
Min |
Max |
Unit |
| Price |
1.83 |
1.83 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
180 |
260 |
MPa |
| Elongation |
4 |
17 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
|
|
|
| Bending strength |
|
|
|
| Hardness |
45 |
75 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
80 |
180 |
MPa |
| Thermal expansion |
24 |
24 |
e-6/K |
| Thermal conductivity |
140 |
140 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
590 |
645 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2650 |
2650 |
kg/m³ |
| Resistivity |
0.049 |
0.049 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Mg 3.1, Mn 0.25, Cr 0.15 (wt.%)) |
|