| Property |
Min |
Max |
Unit |
| Price |
2.06 |
2.29 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
90 |
300 |
MPa |
| Elongation |
5 |
16 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
140 |
155 |
MPa |
| Bending strength |
|
|
|
| Hardness |
30 |
75 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
65 |
250 |
MPa |
| Thermal expansion |
23.4 |
23.5 |
e-6/K |
| Thermal conductivity |
200 |
220 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
575 |
635 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
-100 |
150 |
°C |
| Density |
2630 |
2630 |
kg/m³ |
| Resistivity |
0.06 |
0.06 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
0.1 |
10 |
mm |
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Mg 0.5, Si 0.5, Fe (wt.%)) |
|