| Property |
Min |
Max |
Unit |
| Price |
2.52 |
2.75 |
EURO |
| Young's modulus |
70000 |
70000 |
MPa |
| Shear modulus |
27000 |
27000 |
MPa |
| Tensile strength |
260 |
270 |
MPa |
| Elongation |
8 |
12 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
100 |
105 |
MPa |
| Bending strength |
|
|
|
| Hardness |
60 |
90 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
250 |
250 |
MPa |
| Thermal expansion |
23 |
23.4 |
e-6/K |
| Thermal conductivity |
180 |
220 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
590 |
665 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
-50 |
150 |
°C |
| Density |
2710 |
2710 |
kg/m³ |
| Resistivity |
0.026 |
0.032 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
6 |
10 |
mm |
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Mg 0.6, Si 0.7, Cr, Mn (wt.%)) |
|