| Property |
Min |
Max |
Unit |
| Price |
4.13 |
4.13 |
EURO |
| Young's modulus |
72000 |
72000 |
MPa |
| Shear modulus |
27500 |
27500 |
MPa |
| Tensile strength |
220 |
370 |
MPa |
| Elongation |
12 |
14 |
% |
| Compressive strength |
|
|
|
| Creep strength |
|
|
|
| Fatigue |
|
|
|
| Bending strength |
|
|
|
| Hardness |
80 |
90 |
Brinell |
| Impact strength |
|
|
|
| Yield strength |
200 |
230 |
MPa |
| Thermal expansion |
23 |
23 |
e-6/K |
| Thermal conductivity |
155 |
190 |
W/m.K |
| Specific heat |
960 |
960 |
J/kg.K |
| Melting temperature |
510 |
510 |
°C |
| Glass temperature |
|
|
|
| Service temperature |
|
|
|
| Density |
2710 |
2800 |
kg/m³ |
| Resistivity |
0.034 |
0.043 |
Ohm.mm²/m |
| Breakdown potential |
|
|
|
| Electrochemical potential |
-1.66 |
-1.66 |
V |
| Dielectric loss factor |
|
|
|
| Friction coefficient |
|
|
|
| Refraction index |
|
|
|
| Thickness |
|
|
|
| Shrinkage |
|
|
|
| Water absorption |
|
|
|
|
|
| Remarks |
| (Al rest, Cu 4.0, Mg 0.7, Mn 0.65, Si 0.5 (wt.%)) |
|